Hōʻike Pōkole:

ʻO nā pauka metala he metala i hoʻoliʻiliʻi ʻia i nā huna liʻiliʻi a ʻo ia nā mea kumu kumu no ka hapa nui o nā hana paʻi 3D e hana i nā ʻāpana metallic. ʻO ka paʻi 3D, i ʻike ʻia ma ka hana ʻana i mea hoʻohui (AM), ʻo ia ka hana ʻana i nā ʻāpana a me nā huahana i kahi ʻano papa. ʻO nā ʻano ʻelua o ka pauka metala a me ke ʻano o ke kaʻina paʻi 3D e hoʻoholo ai i nā waiwai o ka huahana hopena. Hana ʻia ka pauka Powder ma muli o ke ʻano o ka hana ʻia ʻana, a he hopena paha ia i nā ʻano kikoʻī a me ka maʻemaʻe.

E hoʻouna leka uila iā mākou Hoʻoiho ma ke ʻano he PDF

ʻIke kikoʻī

Nā huahana huahana

Kuhiliʻole Steel ， ʻAno ； 316L
Nā ʻano o ke kino	nui huna	15-53 μm
	Kinona	Poepoe
	kahekahe	40 S (Mika kahe kahe)
	mānoanoa ʻikea	3.9 Bi / cm3
	Ka mānoanoa	7.98 Bi / cm3

ʻO ka haku mele	Fe	Koena
	Cr	16 ～ 18 wt%
	Ni	10 ～ 14 wt%
	Mo	2 ～ 3 wt%
	Mn	≤2 wt%
	ʻO Si	≤1 wt%
	C	≤0.05 wt%
	P	≤0.045 wt%
	S	≤0.03 wt%
	O	≤0.1 wt%

Nā ʻāpana ʻāpana	Ka mānoanoa pili	Kokoke 99.9%
	Ka ikaika ikaika	Kuhi.560 MPa
	Hua ikaika	Kuhi.480 MPa
	Elongation ma hope o ka haki	Kuhi.20%
	Modulus elasticity	Approx.180 GPa
	ʻOʻoleʻa	Kahi.85 HRB (158 HB)

ʻO ke kinikini aluminika, ʻAno: AlSi10Mg
Nā ʻano o ke kino	nui huna	15-53 μm
	Kinona	Poepoe
	kahekahe	150 S (Mika kahe kahe)
	mānoanoa ʻikea	1.45 Bi / cm3
	Ka mānoanoa	2.67 Bi / cm3

ʻO ka haku mele	Al	Koena
	ʻO Si	9 ～ 10 wt%
	Mg	0.2 ～ 0.45 wt%
	Cu	≤0.05 wt%
	Mn	≤0.45 wt%
	Ni	≤0.05 wt%
	Fe	≤0.55 wt%
	Ti	≤0.15 wt%
	C	≤0.0075wt%

Nā ʻāpana ʻāpana	Ka mānoanoa pili	≥95%
	Ka ikaika ikaika	Kokoke 330 MPa
	Hua ikaika	Kokoke 245 MPa
	Elongation ma hope o ka haki	Kokoke 6%
	Modulus elasticity	Kokoke 70 GPa
	ʻOʻoleʻa	Kokoke 120 HB

ʻO ke kinikini Titanium, ʻAno: TC4 (Ti-6Al-4V)
Nā ʻano o ke kino	nui huna	15-45 μm
	Kinona	Poepoe
	kahekahe	45 S (Mika kahe kahe)
	mānoanoa ʻikea	2.5 Bi / cm3
	Ka mānoanoa	4.51 Bi / cm3

ʻO ka haku mele	Ti	Koena
	Al	5 ～ 6.75 wt%
	V	3.5 ～ 4.5 wt%
	Fe	≤0.25 wt%
	C	≤0.02 wt%
	Y	≤0.005 wt%
	O	0.14 ～ 0.16 wt%
	N	≤0.02 wt%
	Cu	≤0.1 wt%
	Nā ʻē aʻe	0.4 wt%

Nā ʻāpana ʻāpana	Ka mānoanoa pili	Kuhi.99.9%
	Ka ikaika ikaika	Approx.1000 MPa
	Hua ikaika	Kuhi.900 MPa
	Elongation ma hope o ka haki	Kuhi.10%
	Modulus elasticity	Approx.110 GPa
	ʻOʻoleʻa	Kuhi.300 HV (294 HB)

ʻAno superalloy kahua paʻa-nikala: IN718
Nā ʻano o ke kino	nui huna	15-53 μm
	Kinona	Poepoe
	kahekahe	40 S (Mika kahe kahe)
	mānoanoa ʻikea	4.1 Bi / cm3
	Ka mānoanoa	8.15 Bi / cm3

ʻO ka haku mele	Ni	50 ～ 55 wt%
	Cr	17 ～ 22 wt%
	Nb	4.75 ～ 5,5 wt%
	Mo	2.8 ～ 3.3 wt%
	ʻO Co	≤1 wt%
	C	≤0.08 wt%
	P	≤0.015 wt%
	ʻO Si	≤0.35 wt%
	Al	0.2 ～ 0.8 wt%
	Ti	0.65 ～ 1.15 wt%
	Fe	Koena

Nā ʻāpana ʻāpana	Ka mānoanoa pili	≥99%
	Ka ikaika ikaika	Kokoke 980 MPa (1240 MPa ma hope o ka mālama ʻana i ka wela)
	Hua ikaika	Kokoke 780 MPa (1000 MPa ma hope o ka mālama ʻana i ka wela)
	Elongation ma hope o ka haki	12 ～ 30%
	Modulus elasticity	Kokoke 160 GPa
	ʻOʻoleʻa	Kokoke 30 HRC (47 HRC ma hope o ka mālama ʻana i ka wela)

ʻO ke kila hao: ʻAno: MS1
Nā ʻano o ke kino	nui huna	15-53 μm
	Kinona	Poepoe
	kahekahe	40 S (Mika kahe kahe)
	mānoanoa ʻikea	4.3 Bi / cm3
	Ka mānoanoa	8 Bi / cm3

ʻO ka haku mele	Fe	Koena
	ʻO Co	8.5 ～ 9.5 wt%
	Ni	17 ～ 19 wt%
	Mo	4.2 ～ 5.2 wt%
	Mn	≤0.1 wt%
	Ti	0.6 ～ 0.8 wt%
	C	≤0.03 wt%
	Al	0.05 ～ 0.15 wt%
	S	≤0.01 wt%
	Cr	≤0.3 wt%

Nā ʻāpana ʻāpana	Ka mānoanoa pili	≥99%
	Ka ikaika ikaika	Arrpox.1090 MPa (1930 MPa ma hope o ka mālama ʻana i ka wela)
	Hua ikaika	Arrpox.1000 MPa (1890 MPa ma hope o ka mālama ʻana i ka wela)
	Elongation ma hope o ka haki	Arrpox.4%
	Modulus elasticity	Arrpox.160 GPa (180 GPa ma hope o ka mālama ʻana i ka wela)
	ʻOʻoleʻa	Arrpox.35 HRC

Alloy Cobalt-chromium, ʻAno: MP1 (CoCr-2Lc)
Nā ʻano o ke kino	nui huna	15-53 μm
	Kinona	Poepoe
	kahekahe	40 S (Mika kahe kahe)
	mānoanoa ʻikea	4.1 Bi / cm3
	Ka mānoanoa	8.3 Bi / cm3

ʻO ka haku mele	ʻO Co	Koena
	Cr	26 ～ 30 wt%
	Mo	5 ～ 7 uea%
	ʻO Si	≤1 wt%
	Mn	≤1 wt%
	Fe	≤0.75 wt%
	C	≤0.16 wt%
	Ni	≤0.1 wt%

Nā ʻāpana ʻāpana	Ka mānoanoa pili	≥99%
	Ka ikaika ikaika	Approx.1100 MPa
	Hua ikaika	Kuhi.900 MPa
	Elongation ma hope o ka haki	Kuhi.10%
	Modulus elasticity	Kuhi.200 GPa
	ʻOʻoleʻa	35 ～ 45 HRC (323 ～ 428 HB)